Data Sheets

SuperGeo

SuperGeo™ HD Smooth HDPE Nominal Product Specifications

Download PDF

Properties Test Method Minimum Average Values
12 20 30 40 60
Thickness*, (mil.)
Lowest individual reading
ASTM D5199 11
9
18
16
27
24
36
32
54
49
Density, g/cm3 ASTM D1505 .940 .940 .940 .940 .940
Tensile Properties (Each Direction)
Strenght at Break (lbs.)(N/mm)
Strength at Yield (lbs.)(N/mm>
Elongation at Break (%)
Elongation at Yield (%)
ASTM D1505,
Type IV
38 (6)
21 (4)
700
12
68 (12)
38 (6)
700
12
103 (18)
57 (10)
700
12
137 (24)
76 (14)
700
12
205 (36)
113 (20)
700
12
Tear Resistance (lbs.) (N) ASTM D1004 6 (30) 12 (53) 19 (84) 25 (113) 38 (168)
Puncture Resistance (lbs.) (N) ASTM D4833 17 (77) 31 (137) 49 (216) 65 (288) 97 (432)
Carbon Black Content (%) (Range) ASTM 1603 2.0-3.0 2.0-3.0 2.0-3.0 2.0-3.0 2.0-3.0
Carbon Black Dispersion Note(1) Note(1) Note(1) Note(1) Note(1) Note(1)
Standard Roll Dimensions
Length(2), ft 1,850 1,330 1,210 910 600
Width(2), ft 19 19 22 22 22
Area(2), ft 35,150 25,270 26,620 20,020 13,200

(1)9 of 10 views shall be Category 1 or 2. No more than 1 view from Category 3.
(2)Roll widths and lengths have a tolerance of ± 1%
*Custom material thicknesses also available

This data is provided for informational purposes only. Brawler Industries, LLC makes no warranties as to the suitability of the fitness for a specific use or merchantability of products referred to, no guarantee of satisfactory results upon contained information or recommendations and disclaims all liability from resulting loss or damage. This information is subject to change without notice, please check with Brawler Industries, LLC for current updates.

SuperGeo™ Textured HD Nominal Product Specifications

Download PDF

Properties Test Method Frequency Minimum Average Values
30 40 60 80
Thickness, mil

Lowest individual reading 8 of 10 values
Lowest individual for any of 10 values

ASTM D5199 Every Roll Nom. (-10%)

-15%
-20%

Nom. (-10%)

-15%
20%

Nom. (-10%)

-15%
-20%

Nom. (-10%)

-15%
-20%

Density, g/cm3 (minimum) ASTM D1505 200,000 lb .940 .940 .940 .940
Asperity Height, mils ASTM D7466 Every Roll 16 16 16 16
Tensile Properties (Each Direction)
Strength at Break, lb/in width (N/mm)
Strength at Yield lb/in width (N/mm>
Elongation at Break (%)
Elongation at Yield (%)
ASTM D6693,
Type IV
20,000 lb 43 (8)
60 (10)
100
12
57 (10)
80 (14)
100
12
86 (15)
120 (21)
100
12
114 (20)
160 (28)
100
12
Tear Resistance, lb (N) ASTM D1004 45,000 lb 20 (88) 27 (119) 40 (178) 53 (237)
Puncture Resistance, lb (N) ASTM D4833 45,000 lb 43 (190) 57 (254) 86 (380) 114 (507)
Carbon Black Content (%) (Range) ASTM 1603 20,000 lb 2.0 – 3.0 2.0 – 3.0 2.0 – 3.0 2.0 – 3.0
Carbon Black Dispersion ASTM D5596 45,000 lb Note(1) Note(1) Note(1) Note(1)
Standard Roll Dimensions
Roll Length(2), ft 1,020 790 600
Roll Length(2), ft 21.5 21.5 21.5
Roll Area, ft(2) 20,855 16,125 11,180

(1) of 10 readings; 8 of 10 must be ? 14 mils (53mm), and lowest individual reading must be ? 12 mils (30mm)
(1)9 of 10 views shall be Category 1 or 2. No more than 1 view from Category 3.
(2)Roll widths and lengths have a tolerance of  1%
*Custom material thicknesses also available

This data is provided for informational purposes only. Brawler Industries, LLC makes no warranties as to the suitability of the fitness for a specific use or merchantability of products referred to, no guarantee of satisfactory results upon contained information or recommendations and disclaims all liability from resulting loss or damage. This information is subject to change without notice, please check with Brawler Industries, LLC for current updates.

SuperGeo™ HD Smooth

Meets GRI GM13 Specifications

Download PDF

Properties Test Method Minimum Average Values
0.75 1.00 1.50 2.00
Thickness (mm)
Lowest individual reading
ASTM D5199 0.75 mm
-10%
1.00 mm
-10%
1.50 mm
-10%
2.00 mm
-10%
Minimum Density, g/cm³ ASTM D1505 .940 .940 .940 .940
Tensile Properties (1) (Each Direction)
Strength at Break (N)
Strength at Yield (N)
Elongation at Break (%)
Elongation at Yield (%)
ASTM D6693,
Type IV
20
11
700
12
27
15
700
12
40
22
700
12
53
29
700
12
Tear Resistance (N) ASTM D1004 93 125 187 249
Puncture Resistance (N) ASTM D4833 240 320 480 640
Stress Crack Resistance D 5397 500 hr. 500 hr. 500 hr. 500 hr.
Carbon Black Content (%) (Range) ASTM D1603
or D 4218
2.0 – 3.0 2.0 – 3.0 2.0 – 3.0 2.0 – 3.0
Carbon Black Dispersion ASTM D5596 Note (2) Note (2) Note (2) Note (2)
Oxidative Induction Time (OIT) (min. ave.) (3)
(a) Standard OIT
——OR——
(b) High Pressure OIT
D 3895

D 5885

100 min

400 min

100 min

400 min

100 min

400 min

100 min

400 min

Oven Aging at 85°C (3)
(a) Standard OIT (min. ave.) – % retained after 90 days
———-OR————
(b) High Pressure OIT (min. ave.) – % retained after 90 days
D 5721
D 3895

D5885

55%

80%

55%

80%

55%

80%

55%

80%

UV Resistance (4)
(a) Standard OIT (min. ave.)
———-OR———-
(b) High Pressure OIT (min. ave.) – retained after 1600 hrs (6)
D 7238
D 3895

D 5885

N.R. (5)

50%

N.R. (5)

50%

N.R. (5)

50%

N.R. (5)

50%

Standard Roll Dimensions
Roll Length (7) , meters. 332.23 248.41 164.59 121.92
Roll Width (7) , meters. 6.71 6.71 6.71 6.71
Roll Area, meters.2 2229.26 1666.83 1104.39 818.08

(1) Machine direction (MD) and cross machine direction (XMD) average values should be on the basis of 5 test specimens each direction. Yield elongation is calculated using a gage length of 1.3 inches.Break elongation is calculated using a gage length of 2.0 in.
(2) Carbon black dispersion (only near spherical agglomerates) for 10 different views: 9 in Categories 1 or 2 and 1 in Category 3.
(3) Either of the OIT methods listed can be used by the manufacturer to
evaluate the antioxidant content in the geomembrane.
(4) The condition of the test should be 20 hr. UV cycle at 75ËšC followed
by 4 hr. condensation at 60ËšC.
(5) Not recommended since the high temperature of the Std-OIT test
produces an unrealistic result for some of the antioxidants in the UV
exposed samples.
(6) UV resistance is based on percent retained value regardless of the
original HP-OIT value.
(7) Roll Lengths and widths will be +- 1% of the stated dimensions.

This data is provided for informational purposes only. Brawler Industries, LLC makes no warranties as to the suitability or the fitness for a specific use or merchantability of products referred to, no guarantee of satisfactory results upon contained information or recommendations, and disclaims all liability from resulting loss or damage. This information is subject to change without notice, please check with Brawler Industries, LLC for current updates.

SuperGeo™ HD Smooth

Meets GRI GM13 Specifications

Download PDF

Properties Test Method Minimum Average Values
30 40 60 80
Thickness (mil.)
Lowest individual reading
ASTM D5199 30
-10%
40
-10%
60
-10%
80
-10%
Minimum Density, g/cm³ ASTM D1505 .940 .940 .940 .940
Tensile Properties (1) (Each Direction)
Strength at Break (lbs.) (N/mm)
Strength at Yield (lbs.) (N/mm)
Elongation at Break (%)
Elongation at Yield (%)
ASTM D6693,
Type IV
114 (20)
63 (11)
700
12
152 (27)
84 (15)
700
12
228 (40)
126 (22)
700
12
304 (53)
168 (29)
700
12
Tear Resistance (lbs.) (N) ASTM D1004 21 (93) 28 (125) 42 (187) 56 (249)
Puncture Resistance (N) ASTM D4833 54 (240) 72 (320) 108 (480) 144 (640)
Stress Crack Resistance D 5397 500 hr. 500 hr. 500 hr. 500 hr.
Carbon Black Content (%) (Range) ASTM D1603
or D 4218
2.0 – 3.0 2.0 – 3.0 2.0 – 3.0 2.0 – 3.0
Carbon Black Dispersion ASTM D5596 Note (2) Note (2) Note (2) Note (2)
Oxidative Induction Time (OIT) (min. ave.) (3)
(a) Standard OIT
——OR——
(b) High Pressure OIT
D 3895

D 5885

100 min

400 min

100 min

400 min

100 min

400 min

100 min

400 min

Oven Aging at 85°C (3)
(a) Standard OIT (min. ave.) – % retained after 90 days
———-OR————
(b) High Pressure OIT (min. ave.) – % retained after 90 days
D 5721
D 3895

D5885

55%

80%

55%

80%

55%

80%

55%

80%

UV Resistance (4)
(a) Standard OIT (min. ave.)
———-OR———-
(b) High Pressure OIT (min. ave.) – retained after 1600 hrs (6)
D 7238
D 3895

D 5885

N.R. (5)

50%

N.R. (5)

50%

N.R. (5)

50%

N.R. (5)

50%

Standard Roll Dimensions
Roll Length (7) , ft. 1,090 815 540 400
Roll Width (7) , ft. 22 22 22 22
Roll Area, ft.2 23,980 17,930 11,800 8,800

(1) Machine direction (MD) and cross machine direction (XMD) average values should be on the basis of 5 test specimens each direction.
Yield elongation is calculated using a gage length of 1.3 inches.
Break elongation is calculated using a gage length of 2.0 in.
(2) Carbon black dispersion (only near spherical agglomerates) for 10 different views: 9 in Categories 1 or 2 and 1 in Category 3.
(3) Either of the OIT methods listed can be used by the manufacturer to
evaluate the antioxidant content in the geomembrane.
(4) The condition of the test should be 20 hr. UV cycle at 75ËšC followed
by 4 hr. condensation at 60ËšC.
(5) Not recommended since the high temperature of the Std-OIT test
produces an unrealistic result for some of the antioxidants in the UV
exposed samples.
(6) UV resistance is based on percent retained value regardless of the
original HP-OIT value.
(7) Roll Lengths and widths will be +- 1% of the stated dimensions.

This data is provided for informational purposes only. Brawler Industries, LLC makes no warranties as to the suitability or the fitness for a specific use or merchantability of products referred to, no guarantee of satisfactory results upon contained information or recommendations,
and disclaims all liability from resulting loss or damage. This information is subject to change without notice, please check with Brawler Industries, LLC for current updates.

SuperGeo™ HD Textured

Meets GRI GM13 Specifications

Download PDF

Properties Test Method Minimum Average Values
0.75 1.00 1.50 2.00
Thickness (mm)
Lowest individual reading
Lowest individual for any of the 10 values
ASTM D5199 0.75 mm
-10%
-15%
1.00 mm
-10%
-15%
1.50
-10%
-15%
2.00 mm
-10%
-15%
Asperity Height mils (min. ave.) (1) ASTM D1505 16 16 16 16
Minimum Density, g/cm³ ASTM D1505 .940 .940 .940 .940
Tensile Properties (2) (Each Direction)
Strength at Break (N)
Strength at Yield (N)
Elongation at Break (%)
Elongation at Yield (%)
ASTM D6693,
Type IV
8
11
100
12
10
15
100
12
16
22
100
12
213
29
100
12
Tear Resistance (N) ASTM D1004 93 125 187 249
Puncture Resistance (N) ASTM D4833 200 267 400 534
Stress Crack Resistance D 5397 500 hr. 500 hr. 500 hr. 500 hr.
Carbon Black Content (%) (Range) ASTM D1603
or D 4218
2.0 – 3.0 2.0 – 3.0 2.0 – 3.0 2.0 – 3.0
Carbon Black Dispersion ASTM D5596 Note (3) Note (3) Note (3) Note (3)
Oxidative Induction Time (OIT) (min. ave.) (4)
(a) Standard OIT
——OR——
(b) High Pressure OIT
D 3895

D 5885

100 min

400 min

100 min

400 min

100 min

400 min

100 min

400 min

Oven Aging at 85°C (4)
(a) Standard OIT (min. ave.) – % retained after 90 days
———-OR————
(b) High Pressure OIT (min. ave.) – % retained after 90 days
D 5721
D 3895

D5885

55%

80%

55%

80%

55%

80%

55%

80%

UV Resistance (5)
(a) Standard OIT (min. ave.)
———-OR———-
(b) High Pressure OIT (min. ave.) – retained after 1600 hrs (7)
D 7238
D 3895

D 5885

N.R. (6)

50%

N.R. (6)

50%

N.R. (6)

50%

N.R. (6)

50%

Standard Roll Dimensions
Roll Length (8) , meters. 332.23 248.41 164.59 121.92
Roll Width (8) , meters. 6.553 6.553 6.553 6.553
Roll Area, meters.2 2177.10 1863.73 1078.55 798.94

(1) Of 10 readings; 8 of 10 must be ? 0.35 mm, and lowest individual reading must be ?0.30 mm; also see Note 3
(2) Machine direction (MD) and cross machine direction (XMD) average values should beon the basis of 5 test specimens each direction.
Yield elongation is calculated using a gage length of 1.3 inches.
Break elongation is calculated using a gage length of 2.0 in.
(3) Carbon black dispersion (only near spherical agglomerates) for 10 different views:
9 in Categories 1 or 2 and 1 in Category 3.
(4) Either of the OIT methods listed can be used by the manufacturer to
evaluate the antioxidant content in the geomembrane.
(5) The condition of the test should be 20 hr. UV cycle at 75ËšC followed
by 4 hr. condensation at 60ËšC.
(6) Not recommended since the high temperature of the Std-OIT test
produces an unrealistic result for some of the antioxidants in the UV
exposed samples.
(7) UV resistance is based on percent retained value regardless of the
original HP-OIT value.
(8) Roll Lengths and widths will be +- 1% of the stated dimensions.

This data is provided for informational purposes only. Brawler Industries, LLC makes no warranties as to the suitability or the fitness for a specific use or merchantability of products referred to, no guarantee of satisfactory results upon contained information or recommendations,
and disclaims all liability from resulting loss or damage. This information is subject to change without notice, please check with Brawler Industries, LLC for current updates.

SuperGeo™ HD Textured

Meets GRI GM13 Specifications

Download PDF

Properties Test Method Minimum Average Values
30 40 60 80
Thickness (mm)
Lowest individual reading
Lowest individual for any of the 10 values
ASTM D5199 30
-10%
-15%
40
-10%
-15%
60
-10%
-15%
80
-10%
-15%
Asperity Height mils (min. ave.) (1) ASTM D7466 16 16 16 16
Minimum Density, g/cm³ ASTM D1505 .940 .940 .940 .940
Tensile Properties (2) (Each Direction)
Strength at Break (lbs.) (N/mm)
Strength at Yield (lbs.) (N/mm)
Elongation at Break (%)
Elongation at Yield (%)
ASTM D6693,
Type IV
45 (8)
63 (11)
100
12
60 (10)
84 (15)
100
12
90 (16)
126 (22)
100
12
120 (213)
168 (29)
100
12
Tear Resistance (lbs.) (N) ASTM D1004 21 (93) 28 (125) 42 (187) 56 (249)
Puncture Resistance (N) ASTM D4833 45 (200) 60 (267) 90 (400) 120 (534)
Stress Crack Resistance D 5397 500 hr. 500 hr. 500 hr. 500 hr.
Carbon Black Content (%) (Range) ASTM D1603
or D 4218
2.0 – 3.0 2.0 – 3.0 2.0 – 3.0 2.0 – 3.0
Carbon Black Dispersion ASTM D5596 Note (3) Note (3) Note (3) Note (3)
Oxidative Induction Time (OIT) (min. ave.) (4)
(a) Standard OIT
——OR——
(b) High Pressure OIT
D 3895

D 5885

100 min

400 min

100 min

400 min

100 min

400 min

100 min

400 min

Oven Aging at 85°C (4)
(a) Standard OIT (min. ave.) – % retained after 90 days
———-OR————
(b) High Pressure OIT (min. ave.) – % retained after 90 days
D 5721
D 3895

D5885

55%

80%

55%

80%

55%

80%

55%

80%

UV Resistance (5)
(a) Standard OIT (min. ave.)
———-OR———-
(b) High Pressure OIT (min. ave.) – retained after 1600 hrs (7)
D 7238
D 3895

D 5885

N.R. (6)

50%

N.R. (6)

50%

N.R. (6)

50%

N.R. (6)

50%

Standard Roll Dimensions
Roll Length (8) , ft. 1,090 815 540 400
Roll Width (8) , ft. 21.5 21.5 21.5 21.5
Roll Area, ft.2 23,435 17,523 11,610 8,600

(1) Of 10 readings; 8 of 10 must be ? 0.35 mm, and lowest individual reading must be ?
0.30 mm; also see Note 3
(2) Machine direction (MD) and cross machine direction (XMD) average values should be
on the basis of 5 test specimens each direction.
Yield elongation is calculated using a gage length of 1.3 inches.
Break elongation is calculated using a gage length of 2.0 in.
(3) Carbon black dispersion (only near spherical agglomerates) for 10 different views:
9 in Categories 1 or 2 and 1 in Category 3.
(4) Either of the OIT methods listed can be used by the manufacturer to
evaluate the antioxidant content in the geomembrane.
(5) The condition of the test should be 20 hr. UV cycle at 75ËšC followed
by 4 hr. condensation at 60ËšC.
(6) Not recommended since the high temperature of the Std-OIT test
produces an unrealistic result for some of the antioxidants in the UV
exposed samples.
(7) UV resistance is based on percent retained value regardless of the
original HP-OIT value.
(8) Roll Lengths and widths will be +- 1% of the stated dimensions.

This data is provided for informational purposes only. Brawler Industries, LLC makes no warranties as to the suitability or the fitness for a specific use or merchantability of products referred to, no guarantee of satisfactory results upon contained information or recommendations,
and disclaims all liability from resulting loss or damage. This information is subject to change without notice, please check with Brawler Industries, LLC for current updates.

SuperGeo™ LL Smooth LLDPE Nominal Product Specifications

Download PDF

Properties Test Method Frequency Minimum Average Values
12 mil 20 mil 30 mil 40 mil 60 mil
Thickness, mil
Lowest individual reading
ASTM D5199 Per roll 11
9.2
18
16.2
27
24.3
36
32.4
54
48.6
Density, g/cm3 (max) ASTM D1505 200,000 lb .939 .939 .939 .939 .939
Tensile Properties (Each Direction)

Strength at Break, lb/in width (N/mm)
Elongation at Break (%)

ASTM D6693,
Type IV
20,000 lb

39 (6)
800

68 (12)
800

103 (18)
800

137 (24)
800

205 (36)
800

Tear Resistance, lb (N) ASTM D1004 45,000 lb 5 (23) 10 (45) 14 (63) 20 (90) 27 (120)
Puncture Resistance, lb (N) ASTM D4833 14 (63) 25 (112) 38 (171) 50 (225) 72 (320)
Carbon Black Content (%) (Range) ASTM 1603 20,000 lb 2.0 – 3.0 2.0 – 3.0 2.0 – 3.0 2.0 – 3.0 2.0 – 3.0
Carbon Black Dispersion ASTM D5596 45,000 lb Note(1) Note(1) Note(1) Note(1) Note(1)
Standard Roll Dimensions
Roll Length(2), ft 1,850 1,330 1,210 910 600
Roll Length(2), ft 19 19 22 22 22
Roll Area, ft(2) 35,150 25,270 26,620 20,020 13,200

(1)9 of 10 views shall be Category 1 or 2. No more than 1 view from Category 3.
(2)Roll widths and lengths have a tolerance of ± 1%
*Custom material thicknesses also available

This data is provided for informational purposes only. Brawler Industries, LLC makes no warranties as to the suitability of the fitness for a specific use or merchantability of products referred to, no guarantee of satisfactory results upon contained information or recommendations and disclaims all liability from resulting loss or damage. This information is subject to change without notice, please check with Brawler Industries, LLC for current updates.

SuperGeo™ LL Smooth

Meets GRI GM17 Specifications

Download PDF

Properties Test Method Minimum Average Values
0.50 0.75 1.00 1.50 2.00
Thickness (mm)
Lowest individual for any of the 10 values
ASTM D5199 0.50 mm
-10%
0.75 mm
-10%
1.00 mm
-10%
1.50 mm
-10%
2.00 mm
-10%
Density, g/cm³ (max) ASTM D1505 .939 .939 .939 .939 .939
Tensile Properties (1)
Strength at Break, lb/in width (N)
Elongation at Break (%)
ASTM D6693,
Type IV
13
800
20
800
27
800
40
800
53
800
Tear Resistance, (N) ASTM D1004 50 70 100 150 200
Puncture Resistance, (N) ASTM D4833 120 190 250 370 500
Axi-Symmetric Break Resistance Strain – % (min.) ASTM D 5617 30 30 30 30 30
Carbon Black Content, % ASTM D4218 (2) 2.0 – 3.0 2.0 – 3.0 2.0 – 3.0 2.0 – 3.0 2.0 – 3.0
Carbon Black Dispersion ASTM D5596 Note (3) Note (3) Note (3) Note (3) Note (3)
Oxidative Induction Time (OIT) (min. ave.) (4)
(a) Standard OIT
——OR——
(b) High Pressure OIT
D 3895

D 5885

100 min

400 min

100 min

400 min

100 min

400 min

100 min

400 min

100 min

400 min

Oven Aging at 85°C (4)
(a) Standard OIT (min. ave.) – % retained after 90 days
———-OR————
(b) High Pressure OIT (min. ave.) – % retained after 90 days
D 5721
D 3895

D5885

35

60

35

60

35

60

35

60

35

60

UV Resistance (5)
(a) Standard OIT (min. ave.)
———-OR———-
(b) High Pressure OIT (min. ave.) – retained after 1600 hrs (7)
D 7238
D 3895

D 5885

N.R. (6)

35

N.R. (6)

45

N.R. (6)

35

N.R. (6)

35

N.R. (6)

35

Standard Roll Dimensions
Roll Length (8) , meters. 405.38 368.80 277.36 182.88 123.44
Roll Width (8) , meters. 6.705 6.705 6.705 6.705 6.705
Roll Area, meters.2 2718.07 2472.80 1859.69 1226.21 827.66

(1) Machine direction (MD) and cross machine direction (TD) average values should be on
the basis of 5 test specimens each direction.
• Break elongation is calculated using a gage length of 2.0 in at 2.0 in./min
(2) Other methods such at D 1603 (tube furnace) or D 6370 (TGA) are acceptable if an
appropriate correlation to D4218 (muffle furnace) can be established.
(3) Carbon Black dispersion (only near spherical agglomerates) for 10 different views.
• 9 in Categories 1 or 2 and 1 in Category 3
(4) The manufacturer has the option to select either one of the OIT methods listed to evaluate
the antioxidant content in the geomembrane.
(5) The condition of the test should be 20 hr. UV cycle at 75°C followed by 4 hr condensation
at 60°C.
(6) Not recommended since the high temperature of the Std-OIT test produces and
unrealistic result for some of the antioxidants in the UV samples.
(7) UV resistance is based on percent retained value regardless of the original HP-OIT value.
(8) Roll widths and lengths have a tolerance of ± 1%

This data is provided for informational purposes only. Brawler Industries, LLC makes no warranties as to the suitability or the fitness for a specific use or merchantability of products referred to, no guarantee of satisfactory results upon contained information or recommendations,
and disclaims all liability from resulting loss or damage. This information is subject to change without notice, please check with Brawler Industries, LLC for current updates.

SuperGeo™ LL Smooth

Meets GRI GM17 Specifications

Download PDF

Properties Test Method Minimum Average Values
20 mil 30 mil 40 mil 60 mil 80 mil
Thickness, mil (min. ave.)
Lowest individual for any of the 10 values
ASTM D5199 20
-10%
30
-10%
40
-10%
60
-10%
80
-10%
Density, g/cm³ (max) ASTM D1505 .939 .939 .939 .939 .939
Tensile Properties (1)
Strength at Break, lb/in width (mm)
Elongation at Break (%)
ASTM D6693,
Type IV
76
800
114
800
152
800
228
800
304
800
2% Modulus-lb/in. (max.) ASTM D5323 1200 1800 2400 3600 4800
Tear Resistance, (N) ASTM D1004 11 16 22 33 44
Puncture Resistance, (lb) ASTM D4833 28 42 56 84 112
Axi-Symmetric Break Resistance Strain – % (min.) ASTM D 5617 30 30 30 30 30
Carbon Black Content, % ASTM D4218 (2) 2.0 – 3.0 2.0 – 3.0 2.0 – 3.0 2.0 – 3.0 2.0 – 3.0
Carbon Black Dispersion ASTM D5596 Note (3) Note (3) Note (3) Note (3) Note (3)
Oxidative Induction Time (OIT) (min. ave.) (4)
(a) Standard OIT
——OR——
(b) High Pressure OIT
D 3895

D 5885

100

400

100

400

100

400

100

400

100

400

Oven Aging at 85°C (4)
(a) Standard OIT (min. ave.) – % retained after 90 days
———-OR————
(b) High Pressure OIT (min. ave.) – % retained after 90 days
D 5721
D 3895

D5885

35

60

35

60

35

60

35

60

35

60

UV Resistance (5)
(a) Standard OIT (min. ave.)
———-OR———-
(b) High Pressure OIT (min. ave.) – retained after 1600 hrs (7)
D 7238
D 3895

D 5885

N.R. (6)

35

N.R. (6)

45

N.R. (6)

35

N.R. (6)

35

N.R. (6)

35

Standard Roll Dimensions
Roll Length (8) , ft. 1,330 1,210 910 600 405
Roll Width (8) , ft. 22 22 22 22 22
Roll Area, ft.2 29,260 26,620 20,020 13,200 8,910

(1) Machine direction (MD) and cross machine direction (TD) average values should be on
the basis of 5 test specimens each direction.
• Break elongation is calculated using a gage length of 2.0 in at 2.0 in./min
(2) Other methods such at D 1603 (tube furnace) or D 6370 (TGA) are acceptable if an
appropriate correlation to D4218 (muffle furnace) can be established.
(3) Carbon Black dispersion (only near spherical agglomerates) for 10 different views.
• 9 in Categories 1 or 2 and 1 in Category 3
(4) The manufacturer has the option to select either one of the OIT methods listed to evaluate
the antioxidant content in the geomembrane.
(5) The condition of the test should be 20 hr. UV cycle at 75°C followed by 4 hr condensation
at 60°C.
(6) Not recommended since the high temperature of the Std-OIT test produces and
unrealistic result for some of the antioxidants in the UV samples.
(7) UV resistance is based on percent retained value regardless of the original HP-OIT value.
(8) Roll widths and lengths have a tolerance of ± 1%

This data is provided for informational purposes only. Brawler Industries, LLC makes no warranties as to the suitability or the fitness for a specific use or merchantability of products referred to, no guarantee of satisfactory results upon contained information or recommendations,
and disclaims all liability from resulting loss or damage. This information is subject to change without notice, please check with Brawler Industries, LLC for current updates.

SuperGeo™ LL Textured

Meets GRI GM17 Specifications

Download PDF

Properties Test Method Minimum Average Values
0.75 1.00 1.50 2.00
Thickness, mm (min. ave.)
Lowest individual reading 8 out of 10 values
Lowest individual reading for any of 10 values
ASTM D5199 Nom. (-5%)

-10%
-15%

Nom. (-5%)

-10%
-15%

Nom. (-5%)

-10%
-15%

Nom. (-5%)

-10%
-15%

Asperity Height mm (1) (2) (min. ave.) ASTM D7466 0.40 0.40 0.40 0.40
Density, g/cm³ (max) ASTM D1505 .939 .939 .939 .939
Tensile Properties (3) (min. ave.)
Strength at Break, N/mm
Elongation at Break, %
ASTM D6693,
Type IV
9
250
11
250
16
250
21
250
2% Modulus-N/mm. (max.) ASTM D5323 315 420 630 840
Tear Resistance, (N) (min. ave.) ASTM D1004 70 100 150 200
Puncture Resistance, (N) (min. ave.) ASTM D4833 150 200 300 400
Axi-Symmetric Break Resistance Strain – % (min.) ASTM D 5617 30 30 30 30
Carbon Black Content, % ASTM D1603 2.0 – 3.0 2.0 – 3.0 2.0 – 3.0 2.0 – 3.0
Carbon Black Dispersion ASTM D5596 Note (4) Note (4) Note (4) Note (4)
Oxidative Induction Time (OIT) (min. ave.) (5)
(a) Standard OIT
——OR——
(b) High Pressure OIT
D 3895

D 5885

100

400

100

400

100

400

100

400

Oven Aging at 85°C
(a) Standard OIT (min. ave.) – % retained after 90 days
———-OR————
(b) High Pressure OIT (min. ave.) – % retained after 90 days
D 5721
D 3895

D5885

35

60

35

60

35

60

35

60

UV Resistance (6)
(a) Standard OIT (min. ave.)
———-OR———-
(b) High Pressure OIT (min. ave.) – retained after 1600 hrs (8)
D 7238
D 3895

D 5885

N.R. (7)

35

N.R. (7)

45

N.R. (7)

35

N.R. (7)

35

Standard Roll Dimensions
Roll Length (9) , meters 295.65 228.60 158.49 85.34
Roll Width (9) , meters 6.553 6.553 6.553 6.553
Roll Area, meters2 1937.49 1498.01 1038.58 559.23

(1) Of 10 readings; 8 of 10 must be ? 14 mils, and lowest must be ? 12 mils; also see note
(2) Alternate the measurement side for double sided textured sheet
(3) Machine direction (MD) and cross machine direction (TD) average values should be on the
basis of 5 test specimens each direction.
(4) Carbon black dispersion (only near spherical agglomerates) for 10 different views:
• 9 Categories 1 or 2 and 1 Category 3
(5) The manufacturer has the option to select either one of the OIT methods listed to evaluate
the antioxidant content in the geomembrane.
(6) The condition of the test should be 20 hr. UV cycle at 75°C followed by 4 hr. condensation at
60°C.
(7) Not recommended since the high temperature of the Std-OIT test produces an unrealistic
result for some of the antioxidants in the UV exposed samples.
(8) UV resistance is based on percent retained value regardless of the original HP-OIT value
(9) Roll lengths and widths will be ± 1% of the stated dimensions.

This data is provided for informational purposes only. Brawler Industries, LLC makes no warranties as to the suitability or the fitness for a specific use or merchantability of products referred to, no guarantee of satisfactory results upon contained information or recommendations,
and disclaims all liability from resulting loss or damage. This information is subject to change without notice, please check with Brawler Industries, LLC for current updates.

SuperGeo™ LL Textured

Meets GRI GM17 Specifications

Download PDF

Properties Test Method Minimum Average Values
30 mil 40 mil 60 mil 80 mil
Thickness, mm (min. ave.)
Lowest individual reading 8 out of 10 values
Lowest individual reading for any of 10 values
ASTM D5199 Nom. (-5%)

-10%
-15%

Nom. (-5%)

-10%
-15%

Nom. (-5%)

-10%
-15%

Nom. (-5%)

-10%
-15%

Asperity Height mm (1) (2) (min. ave.) ASTM D7466 16 16 16 16
Density, g/ml (max) ASTM D1505 .939 .939 .939 .939
Tensile Properties (3) (min. ave.)
Strength at Break, lb/in
Elongation at Break, %
ASTM D6693,
Type IV
45 (9)
250
60 (11)
250
90 (16)
250
120 (21)
250
2% Modulus-lb/in. (max.) ASTM D5323 1800 2400 3600 4800
Tear Resistance, (N) (min. ave.) ASTM D1004 16 (70) 22 (100) 33 (150) 44 (200)
Puncture Resistance, lb (N) (min. ave.) ASTM D4833 33 (150) 44 (200) 66 (300) 88 (400)
Axi-Symmetric Break Resistance Strain – % (min.) ASTM D 5617 30 30 30 30
Carbon Black Content, % ASTM D1603 2.0 – 3.0 2.0 – 3.0 2.0 – 3.0 2.0 – 3.0
Carbon Black Dispersion ASTM D5596 Note (4) Note (4) Note (4) Note (4)
Oxidative Induction Time (OIT) (min. ave.) (5)
(a) Standard OIT
——OR——
(b) High Pressure OIT
D 3895

D 5885

100

400

100

400

100

400

100

400

Oven Aging at 85°C
(a) Standard OIT (min. ave.) – % retained after 90 days
———-OR————
(b) High Pressure OIT (min. ave.) – % retained after 90 days
D 5721
D 3895

D5885

35

60

35

60

35

60

35

60

UV Resistance (6)
(a) Standard OIT (min. ave.)
———-OR———-
(b) High Pressure OIT (min. ave.) – retained after 1600 hrs (8)
D 7238
D 3895

D 5885

N.R. (7)

35

N.R. (7)

45

N.R. (7)

35

N.R. (7)

35

Standard Roll Dimensions
Roll Length (9) , ft 970 750 520
Roll Width (9) , ft 21.5 21.5 21.5
Roll Area, ft2 20,855 16,1125 11,180

(1) Of 10 readings; 8 of 10 must be ? 14 mils, and lowest must be ? 12 mils; also see note,
(2) Alternate the measurement side for double sided textured sheet
(3) Machine direction (MD) and cross machine direction (TD) average values should be on the
basis of 5 test specimens each direction.
(4) Carbon black dispersion (only near spherical agglomerates) for 10 different views:
• 9 Categories 1 or 2 and 1 Category 3
(5) The manufacturer has the option to select either one of the OIT methods listed to evaluate
the antioxidant content in the geomembrane.
(6) The condition of the test should be 20 hr. UV cycle at 75°C followed by 4 hr. condensation at
60°C.
(7) Not recommended since the high temperature of the Std-OIT test produces an unrealistic
result for some of the antioxidants in the UV exposed samples.
(8) UV resistance is based on percent retained value regardless of the original HP-OIT value
(9) Roll lengths and widths will be ± 1% of the stated dimensions.

This data is provided for informational purposes only. Brawler Industries, LLC makes no warranties as to the suitability or the fitness for a specific use or merchantability of products referred to, no guarantee of satisfactory results upon contained information or recommendations,
and disclaims all liability from resulting loss or damage. This information is subject to change without notice, please check with Brawler Industries, LLC for current updates.

SuperGeo™ Textured LLDPE Nominal Product Specifications

Download PDF

Properties Test Method Frequency Minimum Average Values
30 mil 40 mil 60 mil 80 mil
Thickness, mil

Lowest individual reading 8 of 10 values
Lowest individual for any of 10 values

ASTM D5199 Per Roll Nom. (-10%)

-15%
-20%

Nom. (-10%)

-15%
20%

Nom. (-10%)

-15%
-20%

Nom. (-10%)

-15%
-20%

Density, g/cm3 (Maximum) ASTM D1505 200,000 lb .939 .939 .939 .939
Asperity Height(1) ASTM D7466 Every Roll 16 16 16 16
Tensile Properties (Each Direction)
Strength at Break, lb/in width (N/mm)
Elongation at Break (%)
ASTM D6693,
Type IV
20,000 lb 41 (7)
250
54 (9)
250
81 (14)
250
108 (19)
250
Tear Resistance, lb (N) ASTM D1004 45,000 lb 14 (63) 20 (90) 30 (135) 40 (178)
Puncture Resistance, lb (N) ASTM D4833 45,000 lb 30 (135) 40 (180) 59 (262) 79 (351)
Carbon Black Content (%) (Range) ASTM 1603 20,000 lb 2.0 – 3.0 2.0 – 3.0 2.0 – 3.0 2.0 – 3.0
Carbon Black Dispersion ASTM D5596 45,000 lb Note(2) Note(2) Note(2) Note(2)
Standard Roll Dimensions
Roll Length(2), ft 1,020 790 550
Roll Length(2), ft 21.5 21.5 21.5
Roll Area, ft(2) 21,930 16,985 11,825

(1) of 10 readings; 8 of 10 must be ? 14 mils (53mm), and lowest individual reading must be ? 12 mils (30mm)
(2) 9 of 10 views shall be Category 1 or 2. No more than 1 view from Category 3.
(2)Roll widths and lengths have a tolerance of +/- 1%
*Custom material thicknesses also available

This data is provided for informational purposes only. Brawler Industries, LLC makes no warranties as to the suitability of the fitness for a specific use or merchantability of products referred to, no guarantee of satisfactory results upon contained information or recommendations and disclaims all liability from resulting loss or damage. This information is subject to change without notice, please check with Brawler Industries, LLC for current updates.

SuperScrim

SuperScrim™ D Series

Pro-forma Data Sheet

Download PDF

Properties Test Method Typical Values
Product D8 D12 D20
Thickness, Nominal 8 12 20
Weight (lb/1000 ft2) ASTM D1505 38 58 74
Grab Tensile Strength (lb) ASTM D7004 190 220 250
Grab Tensile Elongation (%) ASTM D7004 30 35 40
Strip Tensile Strength (lb) ASTM D7003 45 53 60
Strip Tensile Elongation (%) @ scrim break ASTM D7003 40 40 40
Strip Tensile Elongation (%) @ film break ASTM D7003 350 670 700
Tongue Tear (lb) ASTM D5884 15 40 53
CBR Puncture (lb) ASTM D6241 280 320 336
Bursting Strength (lb/in2) ASTM D3786 84 105 136
Water Vapor Transmission (WVT) (g/m2-day) ASTM E96 0.40 0.23 0.15
Oxidative Induction Time (OIT)
(a) High Pressure OIT (min.)
ASTM D3895
ASTM D5885
>1000 >1000 >10005
Standard Roll Dimensions
Roll Length, ft 8,000 5,550 4,010
Roll Width, ft 6.167 6.167 6.167
Roll Area, ft2 49,336 33,918.5 24,792.67

Typical values listed in this sheet are representative of initial production runs. These values can be revised anytime without notice as additional test data becomes available.

This data is provided for informational purposes only. Brawler Industries, LLC makes no warranties as to the suitability or the fitness for a specific use or merchantability of products referred to, no guarantee of satisfactory results upon contained information or recommendations,
and disclaims all liability from resulting loss or damage. This information is subject to change without notice, please check with Brawler Industries, LLC for current updates.

SuperScrim™ H Product Specifications

This product meets GRI GM 25 Specifications

Download PDF

Properties Test Method Frequency Minimum Average Values
H30 H36 H45
Thickness,

Nominal (mils)
Min. Ave. (mils)

ASTM D5199 Per Roll 30
27
36
32
45
40
Weight
Nominal (lb/1000, ft2)
Min. Ave. (lb/1000, ft2)
ASTM D5261 Per Roll 140
125
168
151
210
189
Grab Tensile
Strength (lb), min. ave.
Elongation (%), min. ave.
ASTM D7004
(each direction)
(each direction)
30,000 lb 300
25
310
25
310
25
Tongue Tear (lb), min. ave. ASTM D5884
(each direction)
30,000 lb 130 130 130
Index Puncture (lb), min. ave. ASTM D4833 30,000 lb 85 103 105
Ply Adhesion (lb), min. ave.(1) ASTM D6636 35,000 lb 20 25 25
Oxidative Induction Time (OIT)(2)
(a) Standard OIT
or
(b) High Pressure OIT
ASTM D3895

ASTM D5885

Formulation >100

>1000

>100

>1000

>100

>1000

Standard Roll Dimensions
Roll Length(3), ft 11.83 11.83 11.83
Roll Length(3), ft 1500 1230 1000
Roll Area, ft(3) 17,745 14,551 11,830

(1)Alternatively, an acceptable ply adhesion is to have a film tearing bond occur within the sheet material.
(2)The Manufacturer has the option to select either one of the OIT methods listed to evaluate the
antioxidant effectiveness in the geomembrane.
(3)Roll widths and lengths have a tolerance of +/- 1%
*Custom material thicknesses also available
This data is provided for informational purposes only. Brawler Industries, LLC makes no warranties as
to the suitability of the fitness for a specific use or merchantability of products referred to, no guarantee of satisfactory results upon contained information or recommendations and disclaims all liability from resulting loss or damage. This information is subject to change without notice, please check with Brawler Industries, LLC for current updates.
This is a preliminary data sheet based upon laboratory testing of initial manufacturing lots and may be changed without notice as additional product testing data becomes available.

SuperScrim™ WC Product Specifications

Download PDF

Properties Test Method Minimum Average Values
9 mil 12 mil 16 mil 20 mil 24 mil 30 mil
Weight D5261 5.4 oz/yd2 5.7 oz/yd2 7.2 oz/yd2 9.6 oz/yd2 11.5 oz/yd2 13.4 oz/yd2
Thinkness 9 mil 12 mil 16 mil 20 mil 24 mil 30 mil
Grab Tensile (lbs.) D751 MD 200
CD 135
MD 210
CD176
MD 230
CD 210
MD 330
CD 286
MD 352
CD 300
MD 352
CD 300
Mullen Burst D6241 300 psi 350 psi 400 psi 600 psi 680 psi 780 psi
Accelerated UV Weathering D4355 >80% after
2000 hrs
exposure
>90% after
2000 hrs
exposure
>90% after
2000 hrs
exposure
>90% after
2000 hrs
exposure
>90% after
2000 hrs
exposure
>90% after
2000 hrs
exposure
Standard Roll Dimensions
Roll Length(2), ft 3,000 3,000 4,000 3,000 2,250 2,250
Roll Width(2), ft 12 12 12 12 12 12
Roll Area, ft2 36,000 36,000 48,000 36,000 27,000 27,000

(1)9 of 10 views shall be Category 1 or 2. No more than 1 view from Category 3.
(2)Roll widths and lengths have a tolerance of +/- 1%
Custom material thicknesses also available

This data is provided for informational purposes only. Brawler Industries, LLC makes no warranties as
to the suitability of the fitness for a specific use or merchantability of products referred to, no guarantee of satisfactory results upon contained information or recommendations and disclaims all liability from resulting loss or damage. This information is subject to change without notice, please check with Brawler Industries, LLC for current updates.

Material Safety Data Sheets

The OSHA Hazard Communication Standard was recently revised to require that MSDS for hazardous chemical products be updated by June 1, 2015 to meet the updated Globally Harmonized System of Classification and Labelling of Chemicals (GHS) format and content requirements.

All products manufactured and sold by Brawler Industries are not classified as hazardous chemicals under the 1910.1200 rule. Our products meet the OSHA definition of manufactured “articles” that will not expose users to hazardous chemicals under normal and expected conditions of use. Therefore, our products are exempt from all requirements of the rule, including the requirement to produce an MSDS sheet.

For additional information, please visit www.osha.gov (Standard 29 CFR 1910.1200)